Cinkov oksid (ZnO), z različnimi morfologijami smo sintetizirali solvotermalno z različnimi tehnikami. Voda, 1-butanol in etilenglikol so bili uporabljeni kot topila, pri temperaturi od 90 do 120 °C. Resazurin in kofein sta bila uporabljena za vrednotenje fotokatalitske aktivnosti vseh pripravljenih vzorcev (zlasti primerjanje ZnO s komercialnim titanovim dioksidom P25, Evonik Degussa) z uporabo UV spektroskopije. Sestava, kristaliničnost, in morfologija pripravljenih materialov, so bile ugotovljene s FTIR, XRD, TEM in tehniko FEGSEM. Izmerili smo energetsko režo Eg dobljenih polprevodnikov, specifično površino (BET) in poroznost pripravljenih delcev.Velikost kristalov smo določili in ugotovili, da ima pomembno vlogo pri fotokatalizi, ki se je povečala z manjšanjem velikosti delcev. Pri povečani agregaciji smo ugotovili nasprotni učinek. Morfologija delcev je močno vplivala na fotokatalitski proces.
COBISS.SI-ID: 5188890
Poročamo o dvostopenjski proceduri za pripravo nizkotemperaturnih Ni1-xO pigmentnih prevlek z nizko motnostjo, ki so primerne za fleksibilne substrate. S to proceduro najprej pripravimo Ni1-xO pigment iz nikljevega acetata in H2O2-urea raztopine in uporabimo termično obdelavo pri 400°C. Tako pripravljeni pigment smo mleli s cirkonijevimi sferami v vodi in mešanici voda-nikljev oksihidroksi precipitat, ki sočasno delujeta kot dispergator in vezivno sredstvo. Pripravljene suspenzije smo nanesli s tehniko vrtenja na FTO stekla ali fleksibilne ITO-PET folije in plasti tretirali pri 150 °C. Potencialno ciklanje smo izvedli v LiClO4/propilen karbonat in TBA+ triflat/propilen karbonat elektrolitih, kar je pokazalo, da pigmentne prevleke izkazujejo elektrokemijsko in elektrokromno aktivnost tudi v elektrolitu brez litijevih ionov. Poleg tega so variacije v oksidacijskih in redukcijskih pikih pri različnih hitrostih preleta potenciala potrdile prisotnost površinskih elektrokemijskih reakcij.
COBISS.SI-ID: 5335578
The main objective of this study was to broaden the assortment of I-/I3 redox ionic liquids using polyhedral oligomeric silsesquioxanes (PaSS) acting as nanobuilding blocks for the construction of functionalized 1,3-alkylimidazolium iodide solid (melting temperature lSD-200°C) and room temperature (RT) ionic liquids. The structural characteristics of the synthesised final ionic liquids and the corresponding intermediates were determined using 1H, 29Si NMR and infrared spectroscopic measurements. Raman spectra were next reported, in order to demonstrate the presence of polyiodides formed after the addition of iodine and the formation of redox electrolytes. Ionic conductivity values obtained from the impedance (EIS) spectra were determined in the temperature interval from room temperature up to 100°C. Finally, a hybrid electrochromic cell was constructed from room temperature MePrlm+Ix-I07T8 pass (x= 1, 1.2, 3 and 5) ionic liquids encapsulated between a lithiated W03 working and Pt counter-electrode, and colouring-bleaching changes assessed for cells cycled up to 1000 repetitive cycles.
COBISS.SI-ID: 4830746
Raziskali smo omakalne lastnosti hidofobnega bis-ureapropyl-trietoksisililpropil-terminiranega polidimetilsiloksanskega 1000 (PDMSU) sol-gel hibrida, ki tvori pralno obstojne vodoodbojne apreture na bombažnih tkaninah. Dodatek 1H,1H,2H,2H-perfluorooktiltrietoksisilana (PFOTES) k PDMSU daje nizko energijske prevleke na aluminiju. Regenerativna narava olje- in vodoodbojnih lastnosti pranih apretur iz PDMSU-PFOTES je pripisana površinski mobilnosti T8 PFOTES poliedrov.
COBISS.SI-ID: 4133146
V tem delu smo študirali razgradnjo dimetoata z uporabo UV svetlobe in z uporabo LbL tehnike TiO2/polimer pripravljenih hibridnih filmov. Razgradnjo smo spremljali z uporabo HPLC analize in TOC meritev v odvisnosti od časa obsevanja. Popolno razgradnjo dimetoata smo dosegli z dodatkom 4g/L TiO2 in 180 minutnim obsevanjem. Nastanek razgradnih produktov smo potrdili z GCMS. Strupenost obsevanih vzorcev smo ugotavljali z uporabo luminiscenčnih bakterij Vibrio fischeri. Rezultqti so pokazali na povemano strupenost obsevanih vzorcev v primerjavi z izhodno spojino.
COBISS.SI-ID: 1972987