Ni-Ti Shape Memory Alloys (SMAs) have attracted considerable attention as biomaterials for medical devices. However, the biocompatibility of Ni-Ti SMAs is often unsatisfactory due to their poor surface structure. Here we prepared Rapidly Solidified (RS) Ni-Ti SMA ribbons by melt-spinning and their surface was characterised by Auger-electron spectroscopy, X-ray photoelectron spectrometry and scanning electron microscopy. The biocompatibility of the produced ribbons and their immunomodulatory properties were studied on human monocyte-derived dendritic cells (MoDCs). We showed that melt-spinning of Ni-Ti SMAs can form a thin homogenous oxide layer, which improves their corrosion resistance and subsequent toxicity to MoDCs. Ni-Ti RS ribbons stimulated the maturation of MoDCs, as detected by changes in the cells’ morphology and increased expression of HLA-DR, CD86, CD40 and CD83 molecules. However, Ni-Ti RS ribbons enhanced the tolerogenic properties of immature MoDCs, which produced higher levels of IL-10 and IL-27, driving the differentiation of IL-10- and TGF-β-producing CD4+T cells. On the other hand, in the presence of lipopolysaccharide, an important pro-inflammatory biomolecule, Ni-Ti RS ribbons enhanced the allostimulatory and Th1 polarising capacity of MoDCs, whereas the production of Th2 and Th17 cytokines was down-regulated. In conclusion, Ni-Ti RS ribbons possess substantial immunomodulatory properties on MoDCs. These findings might be clinically relevant, because implanted Ni-Ti SMA devices can induce both desired and adverse effects on the immune system, depending on the microenvironmental stimuli.
COBISS.SI-ID: 15705366
The aim of this work was to study the cytotoxicity of different fractions of gold nanoparticles prepared by ultrasonic spray pyrolysis (USP) from gold scrap. The target cells were rat thymocytes, as a type of nonproliferating cells, and L929 mouse fibroblasts, as a type of continuous proliferating cells. Fractions 1 and 2, composed of pure gold nanoparticles, as determined by scanning electron microscopy with a combination of energy dispersive X-ray analysis, were nontoxic for thymocytes, but reduced moderately the proliferative activity of L929 cells. The inhibitory effect of fraction 2, containing particles smaller in size than fraction 1, was stronger. Fraction 3, composed of Au and up to 3% Cu was noncytotoxic for thymocytes, but was cytotoxic for L929 cells. Fraction 4, composed of Au and Ag nanoparticles, and fraction 5, composed of Au together with Cu, Ni, Zn, Fe, and In were cytotoxic for both thymocytes and L929 cells. These results suggest that USP enables the synthesis of pure gold nanoparticles with controlled size, even from gold scrap. However, microstructural analyses and biocompatibility testing are necessary for their proper selection from more cytotoxic gold nanoparticles, contaminated with other elements of gold alloys.
COBISS.SI-ID: 14359830
The results have shown that in the ternary Al94Mn3Cu3 alloy, the phases formed during slower cooling can be predicted by the known Al-Mn-Cu phase diagram. The addition of Be prevented the formation of Al6Mn, decreased the fraction of 1-Al29Mn6Cu4, and increased the fraction of Al4Mn. In the quaternary alloys, the icosahedral quasicrystalline phase dominated by moderate cooling. Heating and annealing of the alloys caused an increase in the volume fractions of 1 in all alloys, and Be4Al(Mn,Cu) in quaternary alloys. Solidification with a moderate cooling rate caused considerable strengthening.
COBISS.SI-ID: 15483926