in hybrid coatings deposited by simultaneous sputtering of silicon and plasma polymerisation of HMDSO + O2 were prepared on glass and steel substrates. oxygen content and surface energy increased with decreasing HMDSO/O2 ratio in hybrid coatings.
COBISS.SI-ID: 797866
Fouling-release coatings were prepared from blends of a fluorinated/siloxane copolymer with a poly(dimethyl siloxane) (PDMS) matrix in order to couple the low modulus character of PDMS with the low surface tension typical for fluorinated polymers. X-ray photoelectron spectroscopy depth profiling analyses were performed .
COBISS.SI-ID: 723626
SiO[sub]x-like coatings were deposited on glass slides from a by plasma-assisted CVD (PACVD). . The most hydrophobic coatings also showed good performance against a freshwater bacterium, Pseudomonas fluorescens
COBISS.SI-ID: 707754
A range of SiO[sub]x-like coatings were deposited on glass slides from a by plasma-assisted CVD resulting coatings were close to SiO[sub]2. For both the removal of sporelings of the marine green alga Ulva linza and the initial adhesion of the freshwater bacterium.
COBISS.SI-ID: 712106
Multilayer Ti(B-N) layers have been sandwiched between a TiN coating on treated AISI H11 steel and an outermost TiB[sub]2 coating. The multilayer coating have been characterized using electron spectroscopy techniques. FE-AES was used to examine the composition of the multilayered films since it has a smaller analysis depth.
COBISS.SI-ID: 699562