The aim of the research was to determine the effect of heat-treatment process parameters on the material properties and their correlations for low-Si-content AISI H11-type hot-work tool steel using a single Circumferentially Notched and fatigue Pre-cracked Tensile Bar (CNPTB) test specimen. The work was also focused on the potential of the proposed approach for designing advanced tempering diagrams and optimizing the vacuum heat treatment, inclulding deep cryogenic treatment, and design of forming tools. The results show that the CNPTB specimen allows a simultaneous determination and correlation of multiple properties for hot-work tool steels, with the compression and bending strength both increasing with hardness, and the strain-hardening exponent and bending strain increasing with the fracture toughness. On the other hand, the best machinability and surface quality of the hardened hot-work tool steel are obtained for hardness values between 46 and 50 HRC and a fracture toughness below 60 MPa?m, obtained by introducing deep cryogenic treatment.
COBISS.SI-ID: 1378730
In this encyclopedia chapter a review on the deep cryogenic treatment process of metallic materials is presented, effect of different influencing parameters (temperature, soaking time, cooling rate) is discussed and presented how the microstructure and properties are changed by cryogenic treatment. Most typical and possible mechanisms behind the changes are presented and discussed from the material type and composition point of view.
COBISS.SI-ID: 1583274
In this review, emphasis is given on ferrous and non-ferrous alloys, which are used as components, where both groups can be treated by deep cryogenic treatment (DCT). DCT has shown to increase hardness, tensile strength and wear resistance, reduce density of defects in crystal structure, improve toughness and corrosion resistance. Though, some researchers also reported results that showed no change in material properties, or even deterioration of material properties, when subjected to DCT. This additionally points out to lack of consistency and reliability of the DCT process, which is needed for its successful incorporation in automotive applications. However, to prove with certainty the resulting outcome on the material properties and knowledge about the reasons for the variation of this effect on metallic materials, further approach and testing with different variables should be conducted in the future. This review provides a synopsis of different approaches of DCT on different materials for automotive applications in order to indicate effects on the material performance during DCT.
COBISS.SI-ID: 1579178